MATERIAL PROPERSTIES
High
Welding Capability
High
Welding Capability
Medium
Bending Capability
Medium
Resistance to Corrosion
CHEMICAL PROPERTIES
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Ga | V | Remarks | Others (Each) | Others (Total) | Aluminium min. |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| EN AW-6061 | 0,4-0,8 | 0.7 | 0,15-0,4 | 0.15 | 0,8-1,2 | 0,04-0,35 | – | 0.25 | 0.15 | – | – | – | 0.05 | 0.15 | Remainder |
MECHANICAL PROPERTIES
6061 - T6
| Thickness (mm) | Tensile Strength (Rm / Mpa) | Yield Strength (Rp0,2) MPa | Elongation min. % A50 mm | Elongation min. % A | Hardness HBWa |
|---|---|---|---|---|---|
| ≤200 | 150 | 110 | 14 | 16 | 65 |
6061 - T651
| Thickness (mm) | Tensile Strength (Rm / Mpa) | Yield Strength (Rp0,2) MPa | Elongation min. % A50 mm | Elongation min. % A | Bend Radiusa 180° | Bend Radiusa 90° | Hardness HBWa |
|---|---|---|---|---|---|---|---|
| 6 < T ≤ 12,5 | 290 | 240 | 9 | 5,0 t | 88 | ||
| 12,5 < T ≤ 40,0 | 290 | 240 | 8 | 88 | |||
| 40 < T ≤ 80 | 290 | 240 | 6 | 88 | |||
| 80 < T ≤ 100 | 290 | 240 | 5 | 88 | |||
| 100 < T ≤ 150 | 275 | 240 | 5 | 84 | |||
| 150 < T ≤ 250 | 265 | 230 | 4 | 81 | |||
| 250 < T ≤ 350 | 260 | 220 | 4 | 80 |
EXTRUSION
| Thickness (mm) | Tensile Strength (Rm / Mpa) | Yield Strength (Rp0,2) MPa | Elongation min. % A50 mm | Elongation min. % A | Bend Radiusa 180° | Bend Radiusa 90° | Hardness HBWa |
|---|---|---|---|---|---|---|---|
| 161,9 < T ≤ 250 | 265 | 230 | 4 | 81 | |||
| 250 < T ≤ 350 | 260 | 220 | 4 | 80 |
SHAPES
Rolled Plate
Rod
Billet
Slab
AREAS OF USE
- Automotive Parts
- Shipbuilding Industry
- Bicycle Parts
- Machine Production
- Medical Equipment
- Aviation Industry
- Fixture Production